Ti-10V-2Fe-3Al is a near beta alloy developed as a high strength forging alloy. This grade provides the best combination of strength and toughness of the commercially available titanium alloys. Its strength permits about a 27% weight savings when compared to Ti-6Al-4V. At the 180 ksi tensile strength level, the K1c value is 40 ksi-in ½ minimum. Solution treated and aged material possesses excellent resistance to stress corrosion cracking, typically K1scc being greater than 0.8 K1c. Solution treated material should not be subject to long term exposure in the 500-800°F range. This could result in high strength but low ductility.

High strength condition: Solution treat 60-100°F below the beta transus (typically 1460-1480°F), not less than 30 minutes, water quench. Age 900-975°F not less than 8 hours, air cool. For lower strength, overage in the 950-1150°F range. This alloy is deep hardenable, capable of high strengths in sections up to approximately 4" thick.

This grade is usually supplied as billet or bar, finish rolled or forged in the alpha-beta field. For the high strength condition, the forging is usually given a pre-form forge above the beta transus, followed by 15-25% reduction below the beta transus.


MIN 9.0 2.6 1.6 - - - - - - - -
MAX 11.0 3.4 2.22 0.05 0.05 0.13 0.015 0.005 0.10 0.30 Balance


AMS 4983AMS 4984AMS 4986AMS 4987
UNS R56410


10V-2Fe-3Al Plate, 10V-2Fe-3Al Round Bar, 10V-2Fe-3Al Sheet

Common Trade Names

10-2-3 Titanium


  • High strength and toughness
  • Weight savings when compared to Ti-6Al-4V
  • Excellent resistance to stress corrosion cracking


  • Hand and die forgings
  • Aircraft landing gear
  • Golf club driver faces

Physical Properties

Density: 0.168 lb/inch³
Nominal Beta Transus: 1470°F
Poisson's ratio: 0.32
Thermal Expansion: 75-800°F, 5.4x10-6 in/in°F
Tensile Modulus: 15.9x106 psi
Modulus: 16.2x106 psi

* 70°F to indicated temperature.

Mechanical Properties

Minimum Mechanical Properties AMS 4984, solution treated and aged

Ultimate Tensile Strength, ksi 173
Ultimate Tensile Strength, ksi 160
0.2% Yield Strength, ksi 4
Reduction of Area, % Report
fracture toughness, k1C 40 ksi

AMS 4987, single solution heat treat & overage

Ultimate Tensile Strength, ksi 140
0.2% Yield Strength, ksi 130
Elongation, % 8
Reduction of Area, % 20
fracture toughness, k1C 80 ksi